環氧地坪漆施工過程中會出現很多問題，環氧地坪漆表層起泡脫層是其中一種常見的問題，特別是南方地區最近連續半個多月的陰雨天氣，空氣中水汽多，地面含水率高，因此環氧地坪漆施工時做好防潮處理工作很重要。環氧地坪漆施工是基礎地面的環境濕度大會滲透到混凝土地面內部，造成地面含水率超標，導致環氧地坪起泡脫層等問題。環氧地坪施工過程中很多因素都會導致地面含水率高，因此環氧地坪漆施工前防潮處理很重要?；鶎映鏊话阌袃蓚€原因，一是新澆筑的混凝土地面養護時間太短，地面未徹底干透，二是施工前清洗地面的水分沒用充分干燥，使得地面含水量過高。

There are many problems in the construction of epoxy floor paint. Foaming delamination of epoxy floor paint surface is one of the common problems. Especially in the rainy and rainy weather in southern China for more than half a month recently, there is much water vapor in the air and high water content on the ground. Therefore, it is very important to do a good job of moisture-proof treatment in the construction of epoxy floor paint. The construction of epoxy floor paint is that the environmental humidity of the foundation ground will penetrate into the interior of the concrete ground, resulting in excessive water content of the ground and foaming delamination of the epoxy floor. During the construction of epoxy flooring, many factors will lead to high water content of the ground. Therefore, moisture-proof treatment before the construction of epoxy flooring paint is very important. There are two reasons for the outflow of base course water. One is that the curing time of newly poured concrete ground is too short and the ground is not thoroughly dry. The other is that the water used to clean the ground before construction is not sufficiently dry, which makes the water content of the ground too high.

要解決這個問題第一就是在施工時設置防水層，防止水直接滲透到基層當中，這樣可以有效的降低含水量。第二是在選擇江西水性環氧環氧地坪材料，水性環氧環氧地坪材料在與基礎地面粘結時不會受到水的影響，防潮涂層可與基面實現有效粘結。第三就是要求施工時防潮層和后續環氧樹脂的粘結強度到達施工要求。

To solve this problem, the first is to set up a waterproof layer during construction to prevent water from penetrating directly into the base, which can effectively reduce the water content. The second is to choose Jiangxi waterborne epoxy flooring materials, waterborne epoxy flooring materials will not be affected by water when bonding with the foundation floor, moisture-proof coating can achieve effective bonding with the base. Thirdly, the bond strength of moisture-proof layer and subsequent epoxy resin is required to meet the construction requirements.